RESUMO
This study evaluated the three-year lifespan of the bond to dentin of experimental self-etch adhesives containing benzodioxole derivatives - 1,3-benzodioxole (BDO) and piperonyl alcohol (PA) - as co-initiator alternative to amines. Adhesive resins were formulated using Bis-GMA, TEGDMA, HEMA, camphorquinone and different co-initiators: BDO, PA or ethyl 4-dimethylamino benzoate (EDAB - amine). An experimental self-etch primer was used to complete the two-step, self-etch adhesive system. Clearfil SE Bond (CSE) was used as commercial reference. Bond strength to human dentin was assessed by microtensile bond strength (µTBS) test, and failure mode was classified. Morphology of the dentin bonding interface was assessed via scanning electron microscopy (SEM). Irrespective of the dental adhesives evaluated, µTBS was higher after 24 hours compared with that after 1.5 and 3 years (p ≤ 0.001). However, adhesives with BDO and PA as co-initiators showed significantly higher bond strength than the bonding resin with EDAB (p ≤ 0.002), independent of the time evaluated. The commercial adhesive CSE showed similar bond strength compared with the other groups (p ≥ 0.05). Mixed failures were mainly observed after 24 hours, while adhesive failures were more frequently observed after 1.5 and 3 years. No notable differences in homogeneity and continuity along the bonded interfaces were detected among the materials in the SEM analysis. In conclusion, benzodioxole derivatives are feasible alternative co-initiators to tertiary amine in camphorquinone-based self-etching dental adhesive formulations.
Assuntos
Benzodioxóis/química , Álcoois Benzílicos/química , Adesivos Dentinários/química , Dentina/efeitos dos fármacos , Dioxóis/química , Cimentos de Resina/química , para-Aminobenzoatos/química , Bis-Fenol A-Glicidil Metacrilato/química , Cânfora/análogos & derivados , Cânfora/química , Colagem Dentária/métodos , Dentina/química , Humanos , Teste de Materiais , Metacrilatos/química , Microscopia Eletrônica de Varredura , Polietilenoglicóis/química , Ácidos Polimetacrílicos/química , Reprodutibilidade dos Testes , Propriedades de Superfície , Resistência à Tração , Fatores de TempoRESUMO
Abstract This study evaluated the three-year lifespan of the bond to dentin of experimental self-etch adhesives containing benzodioxole derivatives - 1,3-benzodioxole (BDO) and piperonyl alcohol (PA) - as co-initiator alternative to amines. Adhesive resins were formulated using Bis-GMA, TEGDMA, HEMA, camphorquinone and different co-initiators: BDO, PA or ethyl 4-dimethylamino benzoate (EDAB - amine). An experimental self-etch primer was used to complete the two-step, self-etch adhesive system. Clearfil SE Bond (CSE) was used as commercial reference. Bond strength to human dentin was assessed by microtensile bond strength (µTBS) test, and failure mode was classified. Morphology of the dentin bonding interface was assessed via scanning electron microscopy (SEM). Irrespective of the dental adhesives evaluated, µTBS was higher after 24 hours compared with that after 1.5 and 3 years (p ≤ 0.001). However, adhesives with BDO and PA as co-initiators showed significantly higher bond strength than the bonding resin with EDAB (p ≤ 0.002), independent of the time evaluated. The commercial adhesive CSE showed similar bond strength compared with the other groups (p ≥ 0.05). Mixed failures were mainly observed after 24 hours, while adhesive failures were more frequently observed after 1.5 and 3 years. No notable differences in homogeneity and continuity along the bonded interfaces were detected among the materials in the SEM analysis. In conclusion, benzodioxole derivatives are feasible alternative co-initiators to tertiary amine in camphorquinone-based self-etching dental adhesive formulations.
Assuntos
Humanos , Álcoois Benzílicos/química , Adesivos Dentinários/química , Cimentos de Resina/química , Dentina/efeitos dos fármacos , Dioxóis/química , Benzodioxóis/química , para-Aminobenzoatos/química , Polietilenoglicóis/química , Ácidos Polimetacrílicos/química , Propriedades de Superfície , Resistência à Tração , Fatores de Tempo , Teste de Materiais , Cânfora/análogos & derivados , Cânfora/química , Microscopia Eletrônica de Varredura , Reprodutibilidade dos Testes , Colagem Dentária/métodos , Bis-Fenol A-Glicidil Metacrilato/química , Dentina/química , Metacrilatos/químicaRESUMO
OBJECTIVES: The purpose of this study was to develop an adhesive resin with incorporation of niobium pentoxide and evaluate its properties. METHODS: Niobium pentoxide was characterised by X-ray diffraction, surface area, particle size, micro-Raman, scanning electron microscopy and the effectiveness of silanisation process by Fourier Transform Infrared (FTIR). An experimental adhesive resin was formulated with 0, 5, 10 and 20wt% Nb(2)O(5). The formulated adhesive resins were evaluated based on microhardness, degree of conversion, radiopacity and interface (resin/dentine) characterisation by micro-Raman. RESULTS: The particles used in this study presented a monoclinic crystalline phase with typical chemical groups and micrometre mean size. Microhardness and radiopacity increased with higher amounts of Nb(2)O(5), and the particles were able to penetrate into the hybrid layers. CONCLUSIONS: Therefore, Nb(2)O(5) may be an alternative for polymer-based biomaterials. CLINICAL SIGNIFICANCE: Niobium pentoxide could be used to produce adhesive resins with enhanced properties.